[摘要]：By using electrochemical activated FTO glass as both a substrate and catalyst, we developed a facile and fast method to fabricate a WO3 center dot 2H(2)O thin film with a thickness of similar to 100 nm. Due to the specific layered crystal structure of the dihydrated phase and the good contact with the transparent conductive oxides (TCOs) layer, the as- prepared WO3 center dot 2H(2)O thin film achieved a fast coloration/bleaching response speed (t(c, 90%) = 3.2 s, t(b, 90%) = 1.2 s), excellent cyclic stability, wide optical modulation range up to 53.8% and a high coloration efficiency of 107.8 cm(2) C-1. A solid-state electrochromic device with a size of 5 cm x 5 cm was also fabricated, exhibiting high transparency contrast and good reversibility between the bleached and colored states. |
|