[摘要]:The mechanical response of a thermally cured Ag nano-ink comprising silver nanoparticles of 3-7 nm diameter was evaluated and compared to a fully dense electron-beam-evaporated Ag film. Curing the nano-ink for 60 min at 250 degrees C resulted in a 78% den