[摘要]：This work reviews and critically discusses the current understanding of two scaling laws, which are ubiquitous in the modeling of monotonic plastic deformation in face-centered cubic metals. A compilation of the available data allows extending the domain of application of these scaling laws to cyclic deformation. The strengthening relation tells that the flow stress is proportional to the square root of the average dislocation density, whereas the similitude relation assumes that the flow stress is inversely proportional to the characteristic wavelength of dislocation patterns. The strengthening relation arises from short-range reactions of non-coplanar segments and applies all through the first three stages of the monotonic stress vs. strain curves. The value of the proportionality coefficient is calculated and simulated in good agreement with the bulk of experimental measurements published since the beginning of the 1960s. The physical origin of what is called similitude is not understood and the related coefficient is not predictable. Its value is determined from a review of the experimental literature. The generalization of these scaling laws to cyclic deformation is carried out on the base of a large collection of experimental results on single and polycrystals of various materials and on different microstructures. Surprisingly, for persistent slip bands (PSBs), both the strengthening and similitude coefficients appear to be more than two times smaller than the corresponding monotonic values, whereas their ratio is the same as in monotonic deformation. The similitude relation is also checked in cell structures and in labyrinth structures. Under low cyclic stresses, the strengthening coefficient is found even lower than in PSBs. A tentative explanation is proposed for the differences observed between cyclic and monotonic deformation. Finally, the influence of cross-slip on the temperature dependence of the saturation stress of PSBs is discussed in some detail. This works takes into account current discussions on the microstructural aspects of cyclic deformation and highlights further work that is required for fully understanding the physical origin of the two scaling laws. (C) 2011 Elsevier Ltd. All rights reserved. |
|