[摘要]:An [001]-oriented BiFeO3 (BFO) thin film having a pseudotetragonal symmetry was epitaxially grown on a Pt/MgO (001) substrate. The Pt-buffered MgO substrate enabled us to fabricate an epitaxial heterostructure at a temperature as low as 500 degrees C. We